Aluminum has many qualities that should make it a suitable material for use in ultra-light and on-chip batteries: it has a high melting point, high conductivity, and low cost.

“It would be a great anode for lithium-ion batteries,” says University of Maryland assistant professor Marina Leite, “if only we could stop it from reacting with lithium ions in a way that quickly ruins them. If we want to solve this problem, we need to understand why and how aluminum anodes fail.”

Leite, a member of the Department of Materials Science and Engineering and the Institute for Research in Applied Physics is part of a team that created a new way to probe the degradation of an entire aluminum anode, in realtime and at nanoscale resolution, using a combination of electron microscopy techniques. What she and her colleagues discovered could give battery developers the insight they need for future success.

All solid-state lithium-ion (Li-ion) batteries require anodes, positively charged electrodes that attract lithium ions during the charging process. These anodes have a “breathing” mechanism: their volume expands by the addition of lithium ions as the battery is being charged, a process called lithiation, then contracts as the ions diffuse back to the positive electrode during discharge, or delithiation process. The anodes must remain stable and able to withstand repeated cycles of charging and discharging without being pulverized in the process.

Prior studies that attempted to explain aluminum anode failure suggested that they either crumbled, which has been observed in other anode materials, or that high strain caused the formation of a stiff aluminum-lithium alloy (AlLi) in the aluminum’s matrix, which ruined its ability to expand and contract properly. Leite and her colleagues devised a way to find out if either of these theories were correct.

“The usual procedure is to take microscopy ‘snapshots' of the anode material before and after cycling the battery,” she explains. “We used a scanning electron microscope to image the changes taking place at the anode while charging and discharging the battery, which established a direct correlation between the structural changes in the material and the electrochemistry.”

Using the new observation technique, Leite and her team discovered that aluminum anode failure is actually caused by lithium reacting with aluminum to form tiny "mounds" on the surface of the aluminum. These structures both permanently trap lithium and block still-free lithium ions from participating in the charge/discharge cycle. The anode’s surface compounded the problem.

“The main challenge of working with aluminum is that a thin layer of aluminum oxide naturally forms on its surface,” says Leite. “In our case, it plays a critical role in the degradation of the battery. When it reacts with the lithium, it forms a very stable alloy, aluminum lithium oxide. The alloy surrounds the mounds, like a prison wall around locked cells. Ultimately, this creates a tough barrier for any remaining lithium ions.”

Without sufficient lithiation and delithiation, the battery’s performance is limited, and since lithium diffuses through aluminum very quickly at room temperature, it doesn’t take long for all these reactions to take place.

Leite’s group is now exploring ways to address these problems, such as developing conductive thin films that will, when applied to surface of an aluminum anode, reduce oxidation and boost the battery’s capacity. The team also hopes to test their observation technique on other battery materials.

A paper describing the observation technique and results of the study was published in the Journal of Materials Chemistry A, where it was also featured on the publication’s inside cover.

For More Information:

See: Marina S. Leite, Dmitry Ruzmetov, Zhipeng Li, Leonid A. Bendersky, Norman C. Bartelt, Andrei Kolmakov and A. Alec Talin. Insights into capacity loss mechanisms of all-solid-state Li-ion batteries with Al anodes. J. Mater. Chem. A, 2014, 2, 20552. View online

Visit the Leite Lab web site



February 23, 2015


«Previous Story  

 

 

Current Headlines

Selected Publications from NanoCenter's AIM Lab and FabLab

Celebrating Women's History Month

Bill Weigand, Former ChBE Faculty Member, Dies at 84

MSAL’s work on serotonin characterization and detection results in two journal covers

Coming of Age in 2023: The 12th Annual Alumni Cup Competition

Maryland Engineers Awarded Grants to Address Humanity's Grand Challenges

New Electrolyte Design Could be the Answer for Safer Rechargeable Batteries even in Extreme Cold

Three UMD Faculty Elected to National Academy of Engineering

Big Ten Network spotlights Maryland Engineering

Maryland Engineers Graham, Nau, Zhao elected Fellows of AAAS

 

Colleges A. James Clark School of Engineering
The College of Computer, Mathematical, and Natural Sciences

Communicate Join Email List
Contact Us
Follow us on TwitterTwitter logo

Links Privacy Policy
Sitemap
RSS

Copyright The University of Maryland University of Maryland
2004-2023